1100 aluminiumsfolie stor rull

$1900-2200 /Ton

Betalings type:	L/C,T/T,D/A,D/P,Paypal
Incoterm:	FOB,CFR,EXW,CIF,FAS
Min. Rekkefølge:	2 Ton
Transport:	Ocean,Land

Kontakt nå

produktbeskrivelse

Produktegenskaper

Emballasje og levering

produktbeskrivelse

Other information

Produktegenskaper

Modell nr.: 1100

Status: Halvhard

Form: Rull

Opprinnelsessted: Kina

Emballasje og levering

Selge enheter

Ton

The file is encrypted. Please fill in the following information to continue accessing it

produktbeskrivelse

produkt introduksjon

Med god formbarhet, korrosjonsbestandighet, termisk ledningsevne og viss styrke, er 1100 aluminiumsfolie mye brukt i varmevekslere i kjøleminæringen, lagringsbeholdere i kjemikalie- og matindustrien, og kondensatorstoffmaterialer i elektronikkindustrien.

GNEE 1100 aluminiumsfolie Fordeler:

1 、 Ren overflate, til og med farge, ingen blomst, flat og ingen pinhole;

2, ikke-giftig og luktfri, trygt og hygienisk;

3 、 Sterke mekaniske egenskaper, høy burst -motstand, punktering og tåremotstand;

4, i prosessen med transport, vær oppmerksom på mobberpakken fuktighet, unngå oksidasjon.
Aluminiumsfolie jumbo rulle

8011 aluminiumsfolierulle
Aluminiumsfolie stor rull

Aluminium 1100 er blant de mykeste aluminiumslegeringene og brukes derfor ikke til høye styrke- eller høytrykksapplikasjoner. Aluminium 1100 kan også sveises. Aluminium 1100 er bare en av flere vanlige aluminiumslegeringer og er myk og lav styrke. Det kan ikke herderes av varmebehandling og er veldig formbar.

Aging:	This material will not age, but can oxidize when left in an extremely damp environment and/or when Exposed to extreme temperatures in both hot and cold environments.
Annealing:	Annealing, which may be necessary after cold working. The material is heated to 650°F and then air cooled.
Applications:	Commonly used as tapes, fin stock, heat exchanger fins, tags, and name plates, commercial filters, decorative applications, giftware, and reflectors, and in sheet metal work.
ASTM Standards:	B479
Cold Working:	This is a excellent alloy for cold working because of the good malleability in the annealed temper. It can easily be bent, drawn, or spun into a variety of applications.
Finish:	Standard Finishes
Forging - Hot Working:	Hot working can be conducted when needed. The alloy can be hot forged.
Forming - Welding:	Forming either hot or cold is readily accomplished with this alloy. In the annealed condition this alloy can be cold worked extensively without an intermediate anneal. Easily welded by all conventional methods.
Hardening:	Hardens during cold working only.
Heat Treatment:	This alloy does not respond to heat treatment other than to anneal the material into a soft or O Temper material.
Other Physical Properties:	Electrical conductivity is 53% of copper.
Principal Design Features:	This alloy is 99.0% min pure aluminum with excellent ability to be formed and worked.
QQA Standards:	1876
Temper:	This material is available in a variety of tempers.
Thickness:	0.0005 to 0.064 in
Width:	0.375 to 60 in

Stanford Advanced Materials ønsker velkommen til enhver mulighet i aluminiumsfolie, aluminiumspole eller arkprodukter du måtte trenge. Spesifikasjonene som vises på disse sidene er ikke til designformål. Du kan kontakte oss for mer informasjon.

Al	99.0~99.95%
Cu	0.05~0.20%
Fe	≤0.95%
Mn	≤0.05%
Si	≤0.95%
Zn	≤0.1%
Residuals	≤0.15%

Aluminiumslegering 1100 Folie Mekaniske egenskaper

Elongation (Annealed): ¹	35
Elongation (H12):	12
Elongation (H14):	9
Elongation (H16):	6
Elongation (H18):	5
Other Mechanical Properties:	Shear strength values are: “O” (annealed) temper 9 KSI, H12 temper 10 KSI, H18 temper 13 KSI.
Tensile Strength (Annealed): ²	13 x 1000 psi
Tensile Strength (H12):	16 x 1000 psi
Tensile Strength (H14):	18 x 1000 psi
Tensile Strength (H16):	21 x 1000 psi
Tensile Strength (H18):	24 x 1000 psi
Yield Strength (Annealed): ³	5 x 1000 psi
Yield Strength (H12):	15 x 1000 psi
Yield Strength (H14):	17 x 1000 psi
Yield Strength (H16):	20 x 1000 psi
Yield Strength (H18):	22 x 1000 psi