Modell nr.: Zirconium Alloy
Merke: Gnee
Opprinnelsessted: Kina
Shape: Round Bar
Alloy: Alloy
sertifisering: ISO, RoHS, IBR, AISI, ASTM, GB, EN, DIN, JIS
Moq: 1ton
Technology: Cold Rolling Hot Rolling
Specification: Zirconium and zirconium alloy rods
| Selge enheter | : | Ton |
| Pakketype | : | Standard luftverdig emballasje |
| Eksempel på bilde | : |
|
The file is encrypted. Please fill in the following information to continue accessing it
Zirconium Rod Uns R60705 Round Rod
UNS R60705 zirkonium har lav termisk nøytronabsorpsjonstverrsnitt, høy styrke og hardhet, utmerket korrosjonsmotstand og duktilitet. Det er mye brukt innen atomenergiindustrien, romfart og biomedisin. Det er et viktig strategisk materiale, også kjent som "nummer én metall i atomalderen". For ytterligere å øke stabiliteten til bruk av zirkoniumlegering og redusere behandlings- og produksjonsvansker, er det viktig å koble zirkoniumlegeringsmaterialer. Derfor er det avgjørende å studere strukturen og egenskapene til zirkoniumlegeringstilkoblinger etter at de er dannet gjennom sveiseteknologi, og diffusjonssveising brukes som en vanlig materiale som sammenføyningsmetode som kan brukes til sveising av zirkonium og zirkoniumlegeringer.
Vi kan tilby: zirkoniumlegeringer, titanlegeringer, Niobium -legering og andre produkter.
Kjemiske egenskaper til zirkoniumlegering 705 runde barer:
| Grade | Zr+Hf | Hf | Fe+Cr | Sn | H | N | C | O | Nb |
| R60702 | 99.2% | <4.5% | <0.20% | - | <0.005% | <0.015% | <0.030% | <0.15% | - |
| R60704 | 97.5% | <4.5% | 0.2-0.4% | 1.0-2.0% | <0.005% | <0.015% | <0.030% | <0.16% | - |
| R60705 | 95.5% | <4.5% | <0.2% | - | <0.005% | <0.015% | <0.050% | <0.16% | 2.0-3.0% |
Mekanisk diagram over R60705 Zirconium Alloy sveisestang:
| Molecular Weight | 91.22 |
|---|---|
| Appearance | White |
| Melting Point | 1852 °C |
| Boiling Point | 3580 °C |
| Density | 6506 kg/m3 |
| Solubility in H2O | N/A |
| Electrical Resistivity | 40.0 microhm-cm @ 20 oC °C |
| Electronegativity | 1.4 Paulings |
| Heat of Fusion | 5.50 Cal/gm mole |
| Heat of Vaporization | 120 K-Cal/gm atom at 4377 °C |
| Poisson's Ratio | 0.34 |
| Specific Heat | 0.0671 Cal/g/K @ 25 oC °C |
| Tensile Strength | 230 MPa |
| Thermal Conductivity | 0.227 W/cm/K @ 298.2 K |
| Thermal Expansion | (25 °C) 5.7 µm·m-1·K-1 |
| Vickers Hardness | 903 MPa |
| Young's Modulus | 88 GPa |
R60705 zirkoniumlegering rundt bar Arkivproduktbilde:
Kontakt oss
Personvernerklæring: Ditt personvern er veldig viktig for oss. Vårt selskap lover å ikke røpe din personlige informasjon til noen ekspanien til de eksplisitte tillatelsene dine.
Fyll ut mer informasjon slik at det kan komme i kontakt med deg raskere
Personvernerklæring: Ditt personvern er veldig viktig for oss. Vårt selskap lover å ikke røpe din personlige informasjon til noen ekspanien til de eksplisitte tillatelsene dine.
Contact Now